| Citation: | XU C，XIAO Y，DENG P C. Fatigue life prediction of CFRP flat-joggle-flat bonded joint[J]. Journal of Beijing University of Aeronautics and Astronautics，2025，51（2）：518-524 （in Chinese） doi: 10.13700/j.bh.1001-5965.2023.0048
|
Parameter fitting was done using tests for the cohesive model, the normalized fatigue life model, the stiffness degradation model of the unidirectional laminate, and carbon fiber reinforced polymer (CFRP) flat-joggle-flat (FJF) bonded joint. Based on the models mentioned above, the fatigue life of the bonded joint was predicted by using ABAQUS software. Results show that under a certain maximum load, the predicted adhesive cracking life at the end of the overlap zone and the ultimate fatigue life of the bonded joint have an error value of no more than 3%, compared with the corresponding test results, which illustrates good accuracy. It is evident that the adhesive cracking life plays a major role and that the adhesive crack propagation life can be disregarded because the adhesive cracking life at the end of the overlap zone is almost equal to the ultimate fatigue life of the bonded joint.
| [1] |
韩子健, 周金宇, 庄百亮, 等. 复合材料件单搭接胶接结构可靠性分析[J]. 机械设计与制造, 2023, 385(3): 63-66. doi: 10.3969/j.issn.1001-3997.2023.03.014
HAN Z J, ZHOU J Y, ZHUANG B L, et al. Reliability analysis of single lap adhesive structure of composite material[J]. Machinery Design & Manufacture, 2023, 385(3): 63-66(in Chinese). doi: 10.3969/j.issn.1001-3997.2023.03.014
|
| [2] |
宗俊达, 姚卫星. FRP复合材料剩余刚度退化复合模型[J]. 复合材料学报, 2016, 33(2): 280-286.
ZONG J D, YAO W X. Compound model of residual stiffness degradation for FRP composites[J]. Acta Materiae Compositae Sinica, 2016, 33(2): 280-286(in Chinese).
|
| [3] |
陈基伟, 姚卫星, 宗俊达, 等. 复合材料剩余刚度概率模型研究[J]. 南京亚洲成人在线一二三四五六区学报, 2019, 51(4): 534-539.
CHEN J W, YAO W X, ZONG J D, et al. Probability model of residual stiffness of composite materials[J]. Journal of Nanjing University of Aeronautics & Astronautics, 2019, 51(4): 534-539(in Chinese).
|
| [4] |
PAKDEL H, MOHAMMADI B. Stiffness degradation of composite laminates due to matrix cracking and induced delamination during tension-tension fatigue[J]. Engineering Fracture Mechanics, 2019, 216: 106489. doi: 10.1016/j.engfracmech.2019.106489
|
| [5] |
吴坤岳. 基于内聚力模型的胶接结构疲劳特性研究[D]. 大连: 大连理工大学, 2013.
WU K Y. Study on fatigue characteristics of bonded structure based on cohesion model[D]. Dalian: Dalian University of Technology, 2013(in Chinese).
|
| [6] |
DE MOURA M F S F, GONÇALVES J P M. Cohesive zone model for high-cycle fatigue of composite bonded joints under mixed-mode I+II loading[J]. Engineering Fracture Mechanics, 2015, 140: 31-42. doi: 10.1016/j.engfracmech.2015.03.044
|
| [7] |
AL-AZZAWI A S M, KAWASHITA L F, FEATHERSTON C A. A modified cohesive zone model for fatigue delamination in adhesive joints: numerical and experimental investigations[J]. Composite Structures, 2019, 225: 111114. doi: 10.1016/j.compstruct.2019.111114
|
| [8] |
KISHORE A N, PRASAD N S. An experimental study of flat-joggle-flat bonded joints in composite laminates[J]. International Journal of Adhesion and Adhesives, 2012, 35: 55-58. doi: 10.1016/j.ijadhadh.2012.02.003
|
| [9] |
许昶, 刘志明. CFRP平-折-平连接接头试验研究与数值模拟[J]. 北京亚洲成人在线一二三四五六区学报, 2019, 45(11): 2207-2216.
XU C, LIU Z M. Experimental study and numerical simulation on CFRP flat-joggle-flat joints[J]. Journal of Beijing University of Aeronautics and Astronautics, 2019, 45(11): 2207-2216(in Chinese).
|
| [10] |
HARRIS B, GATHERCOLE N, LEE J A, et al. Life-prediction for constant-stress fatigue in carbon-fibre composites[J]. Philosophical Transactions of the Royal Society of London Series A, 1997, 355(1727): 1259-1294. doi: 10.1098/rsta.1997.0055
|
| [11] |
SHOKRIEH M M, LESSARD L B. Progressive fatigue damage modeling of composite materials, Part I: Modeling[J]. Journal of Composite Materials, 2000, 34(13): 1056-1080. doi: 10.1177/002199830003401301
|
| [12] |
国家质量监督检验检疫总局, 中国国家标准化管理委员会. 纤维增强塑料性能试验方法总则: GB/T 1446—2005[S]. 北京: 中国标准出版社, 2005.
General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, Standardization Administration of the People’s Republic of China. Fiber-reinforced plastics composites? The generals: GB/T 1446—2005[S]. Beijing: Standards Press of China, 2005(in Chinese).
|
| [13] |
国防科学技术工业委员会. 碳纤维树脂基复合材料层合板疲劳试验方法: GJB 2637—1996[S]. 北京: 国家军用标准出版发行部, 1996.
Commission of Science, Technology and Industry for National Defense. Test method for fatigue of carbon fiber resin matrix composite laminates: GJB 2637—1996[S]. Beijing: National Military Standards Publishing and Distribution Department, 1996(in Chinese).
|
| [14] |
沈观林. 复合材料力学[M]. 北京: 清华大学出版社, 1996: 134-136.
SHEN G L. Mechanics of composite materials[M]. Beijing: Tsinghua University Press, 1996: 134-136(in Chinese).
|
| [15] |
GATHERCOLE N, REITER H, ADAM T, et al. Life prediction for fatigue of T800/5245 carbon-fibre composites: I. Constant-amplitude loading[J]. International Journal of Fatigue, 1994, 16(8): 523-532. doi: 10.1016/0142-1123(94)90478-2
|
| [16] |
王丹勇. 层合板接头损伤失效与疲劳寿命研究[D]. 南京: 南京亚洲成人在线一二三四五六区, 2006.
WANG D Y. Study on damage failure and fatigue life of laminated plate joints[D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2006(in Chinese).
|
| [17] |
YANG J N, JONES D L, YANG S H, et al. A stiffness degradation model for graphite/epoxy laminates[J]. Journal of Composite Materials, 1990, 24: 753-769 . doi: 10.1177/002199839002400705
|
| [18] |
LEE J H. An experimental and analytical investigation of the stiffness degradation of graphite/epoxy composite laminates under cyclic loading[D]. Washington, D. C. : The George Washington University, 1989.
|
| [19] |
SHENOY V, ASHCROFT I A, CRITCHLOW G W, et al. An investigation into the crack initiation and propagation behaviour of bonded single-lap joints using backface strain[J]. International Journal of Adhesion and Adhesives, 2009, 29(4): 361-371. doi: 10.1016/j.ijadhadh.2008.07.008
|
| [20] |
刘建明, 万小朋, 赵美英. 层合板螺栓连接结构疲劳寿命预测[J]. 航空学报, 2015, 36(6): 1867-1875.
LIU J M, WAN X P, ZHAO M Y. Fatigue life prediction of laminated bolted joint structures[J]. Acta Aeronautica et Astronautica Sinica, 2015, 36(6): 1867-1875(in Chinese).
|
Figures(9) / Tables(8)
Copyright © Journal of Beijing University of Aeronautics and Astronautics
Address: Editorial Department of Journal of Beijing University of Aeronautics and Astronautics, 37 Xueyuan Road, Haidian District, Beijing Post Code: 100191 Email: jbuaa@cqjj8.com
Supported by:
Beijing Renhe Information Technology Co., Ltd.
DownLoad: